Wir verwenden Cookies, um für diese Website Funktionen wie z.B. Login, einen Warenkorb oder die Sprachwahl zu ermöglichen. Weiterhin nutzen wir für anonymisierte, statistische Auswertungen der Nutzung Google Analytics, welches Cookies setzt. Mehr Informationen finden Sie in unserer Datenschutzerklärung.
OK, ich bin einverstanden Ich möchte keine Google Analytics-Cookies
Quintessence International
Login:
Benutzername:

Kennwort:

Plattform:

Kennwort vergessen?

Registrieren

Quintessence Int 41 (2010), Nr. 6     27. Apr. 2010
Quintessence Int 41 (2010), Nr. 6  (27.04.2010)

Online Article, Seite 527, PubMed:20490385, Sprache: Englisch


Online Article: Shear bond strength of composite bonded with three adhesives to Er,Cr:YSGG laser-prepared enamel
Türkmen, Cafer / Sazak-Öveçoglu, Hesna / Günday, Mahir / Güngör, Gülsad / Durkan, Meral / Öksüz, Mustafa
Objective: To assess in vitro the shear bond strength of a nanohybrid composite resin bonded with three adhesive systems to enamel surfaces prepared with acid and Er,Cr:YSGG laser etching.
Method and Materials: Sixty extracted caries- and restoration-free human maxillary central incisors were used. The teeth were sectioned 2 mm below the cementoenamel junction. The crowns were embedded in autopolymerizing acrylic resin with the labial surfaces facing up. The labial surfaces were prepared with 0.5-mm reduction to receive composite veneers. Thirty specimens were etched with Er,Cr:YSGG laser. This group was also divided into three subgroups, and the following three bonding systems were then applied on the laser groups and the other three unlased groups: (1) 37% phosphoric acid etch + Bond 1 primer/adhesive (Pentron); (2) Nano-bond self-etch primer (Pentron) + Nano-bond adhesive (Pentron); and (3) all-in-one adhesive-single dose (Futurabond NR, Voco). All of the groups were restored with a nanohybrid composite resin (Smile, Pentron). Shear bond strength was measured with a Zwick universal test device with a knife-edge loading head. The data were analyzed with two-factor ANOVA.
Results: There were no significant differences in shear bond strength between self-etch primer + adhesive and all-in-one adhesive systems for nonetched and laser-etched enamel groups (P > .05). However, bond strength values for the laser-etched + Bond 1 primer/adhesive group (48.00 ± 13.86 MPa) were significantly higher than the 37% phosphoric acid + Bond 1 primer/adhesive group (38.95 ± 20.07 MPa) (P < .05).
Conclusion: The Er,Cr:YSGG laser-powered hydrokinetic system etched the enamel surface more effectively than 37% phosphoric acid for subsequent attachment of composite material.

Schlagwörter: enamel etching, Er,Cr:YSGG laser, shear bond strength