Wir verwenden Cookies, um für diese Website Funktionen wie z.B. Login, einen Warenkorb oder die Sprachwahl zu ermöglichen. Weiterhin nutzen wir für anonymisierte, statistische Auswertungen der Nutzung Google Analytics, welches Cookies setzt. Mehr Informationen finden Sie in unserer Datenschutzerklärung.
OK, ich bin einverstanden Ich möchte keine Google Analytics-Cookies
Quintessence International
Login:
Benutzername:

Kennwort:

Plattform:

Kennwort vergessen?

Registrieren

Quintessence Int 38 (2007), Nr. 9     31. Aug. 2007
Quintessence Int 38 (2007), Nr. 9  (31.08.2007)

Online Article, Seite 797, PubMed:17873972, Sprache: Englisch


Online Article: Diametral tensile strength of dual-curing resin cements submitted exclusively to autopolymerization
Fonseca, Renata Garcia / Artusi, Thais Paci / Santos, Juliana Gomes dos / Adabo, Gelson Luis
Objectives: To evaluate, at different times, the diametral tensile strength (DTS) of dual-curing resin cements that were not photopolymerized.
Method and Materials: Equal amounts of base and catalyst pastes of Panavia F (Kuraray), Variolink II (Vivadent), Rely X (3M ESPE), and Enforce (Dentsply) were mixed and inserted into cylindrical molds (4 3 2 mm) (n = 10). Cements were not photopolymerized. DTS test was performed in a testing machine at 30 minutes, 1 hour, 24 hours, and 7 days. The specimens were stored in light-proof containers with distilled water at 37°C until the time of assay. An autopolymerizing resin cement (Cement-It, Jeneric Pentron) and a zinc phosphate cement served as controls. One-way analysis of variance (ANOVA) and Tukey test were performed separately for each cement and for each time (P < .05).
Results: All cements showed an increase in DTS when tested at 1 and 24 hours. Tests at 24 hours and 7 days revealed no statistically significant differences. In all groups, the zinc phosphate cement had the lowest DTS mean values (2.1 MPa, 3.6 MPa, 6.5 MPa, and 6.9 MPa), while Cement-It (35.1 MPa, 33.6 MPa, 46.9 MPa, and 46.3 MPa) and Enforce (31.9 MPa, 31.7 MPa, 43.4 MPa, and 47.6 MPa) presented the highest DTS mean values.
Conclusion: All cements presented maximal strength at 24 hours. The dual-curing resin cements, even when nonphotopolymerized, demonstrated higher DTS than the zinc phosphate cement and similar or lower values than the autopolymerizing resin cement.

Schlagwörter: autopolymerization, diametral tensile strength, dual-curing resin cements, mechanical properties, metallic restorations, polymerization modes